【正文】 ，采用氯乙酸處理纖維素纖維來制備羧甲基纖維素纖維。通過控制氯乙酸和纖維的質(zhì)量比得到不同反應程度的羧甲基纖維素纖維。實驗結(jié)果顯示，由于處理后纖維的結(jié)構(gòu)中含有高吸水性的羧甲基基團，處理后的纖維比初始纖維有更高的吸濕性。當被加工成醫(yī)用敷料后，這種具有高吸濕性的羧甲基纖維素纖維可以吸收大量的傷口滲出液。羧甲基纖維素纖維可以把液體吸收進纖維內(nèi)部，使纖維在吸濕后轉(zhuǎn)化成一種水凝膠體，在傷口上可以形成一個適合創(chuàng)面愈合的潮濕環(huán)境，在傷口護理中有很高的應用價值。關(guān)鍵詞：醫(yī)用敷料； 纖維素纖維； 羧甲基化； 愈合環(huán)境ABSTRACTIn order to impmve the hydroscopic property of fibers， cellulose fibers were treated with chloroacetic acid to prepare carboxymethyl cellulose fibers. Fibers with different degrees of carboxymethylation were prepared by controlling the ratio of the weight of fiber to chlomacetic acid．Experimental results showed that the treated fibers had much higher hydroscopicity than the untreated ones，due to the highly absorbent carboxymethyl groups in the fiber structure. When made into wound dressings, these highly absorbent carboxymethyl fibers can absorb a large amount of wound fluid. The results of this study confirmed that carboxymethylated cellulose fibers absorb liquid into the inside of fiber，and bee a hydrogel when being wet．Because they can create a moist environment suitable for wound healing, this type of pmduct is highly valuable in wound care．Key words：wound dressing。 cellulose fiber。 carboxymethylation。 healing environment目 錄1. 前言 ……………………………………………………………………………1 纖維素及其衍生物概述…………………………………………………1 纖維素材料簡述………………………………………………………1 CMC的研究進展……………………………………………………2 國內(nèi)CMC的生產(chǎn)和貿(mào)易現(xiàn)狀……………………………………3 羧甲基纖維素制備…………………………………………………4 羧甲基纖維素的制備原理…………………………………………4 羧甲基纖維素的制備工藝…………………………………………5 水媒法工藝…………………………………………………………5 溶媒法工藝…………………………………………………………6 羧甲基纖維素的應用……………………………………………………7 CMC在醫(yī)藥行業(yè)中的應用………………………………………7 CMC在食品工業(yè)中的應用………………………………………8 CMC在其他工業(yè)中的應用………………………………………8 實驗目的和意義…………………………………………………………9 實驗目的…………………………………………………………………9 實驗意義…………………………………………………………………92. 實驗部分……………………………………………………………………10 實驗材料、化學品及儀器…………………………………………10 實驗材料……………………………………………………………10 實驗所需化學品……………………………………………………10 實驗儀器……………………………………………………………10 實驗步驟及方案………………………………………………………11 實驗所需溶液………………………………………………………11 浸軋法的實驗步驟…………………………………………………11 實驗方案……………………………………………………………11 實驗內(nèi)容…………………………………………………………………12 制備實驗樣品…………………………………………………………12 取代度測試……………………………………………………………12 吸濕性測試……………………………………………………………12 拉伸斷裂測試…………………………………………………………13 透氣性測試……………………………………………………………13 耐磨損性測試…………………………………………………………13 抗菌性測試……………………………………………………………133. 實驗數(shù)據(jù)及分析…………………………………………………………13 確定一溶液最佳堿濃度…………………………………………………13 取代度、吸濕性測試結(jié)果及分析………………………………13 拉伸斷裂、透氣、耐磨損性能測試結(jié)果及分析……………14 抗菌性能測試結(jié)果及分析…………………………………………17 小結(jié)……………………………………………………………………17 確定堿與酸的最佳摩爾比……………………………………………17 取代度、吸濕性測試結(jié)果及分析………………………………17 拉伸斷裂、透氣、耐磨損性能測試結(jié)果及分析……………18 小結(jié)……………………………………………………………………21 樣品結(jié)構(gòu)…………………………………………………………………214. 結(jié)論……………………………………………………………………………22參考文獻…………………………………………………………………………231 前言 羧甲基纖維索鈉(carboxymethylcellulose，CMC)，由德國于1918年首先制得并于1921年獲準專利而見諸于世。此后便在歐洲實現(xiàn)商業(yè)化生產(chǎn)。當時只為粗產(chǎn)品用作膠體和粘結(jié)劑。1936~1941年，羧甲基纖維素鈉的工業(yè)應用研究相當活躍，明了幾個相當有啟發(fā)性的專利。第二次世界大戰(zhàn)期問，德國將羧甲基纖維素鈉用于成洗滌劑。Hercules公司于1943年為美國首次制成羧甲基纖維素鈉，并于1946年生產(chǎn)精制的羧甲基纖維素鈉產(chǎn)品[1~2]。 纖維素及其衍生物概述 纖維素材料纖維素來源于樹木、棉花、麻類植物和其它農(nóng)副產(chǎn)品，是自然界中取之不盡用之不竭的可再生資源，是高分子化學誕生和發(fā)展時期的主要研究對象。在纖維素結(jié)構(gòu)中存在的OH，為纖維素進行化學改性提供了物質(zhì)基礎，而纖維素衍生物則是高分子化學中最早研究和生產(chǎn)的一大類產(chǎn)品，它是將天然高分子纖維素經(jīng)化學方法處理而制成的用途廣泛的高分子精細化工材料。作為纖維素中重要的一類衍生物，纖維素醚類產(chǎn)品更是具有廣闊的發(fā)展前途，隨著新的產(chǎn)品不斷研制出來，纖維素醚產(chǎn)品新的用途也在不斷的被發(fā)現(xiàn)并涉及到許多工業(yè)領域，被人們普遍稱為“工業(yè)味精”。但是，由于20世紀50年代后期石油化工的興起，許多新的合成高分子材料研制成功并大規(guī)模工業(yè)化生產(chǎn)，使得纖維素衍生物在高分